Mara Colored Stone
Dry Mix Finishes
Mara colored stone is an innovative wall decoration material made from a mixture of dry powder materials such as natural mineral particles, cement, quartz sand, inorganic pigments, and polymer additives. It combines artistic expression with practical functionality. By simulating the texture and color of natural stone and incorporating modern coating technology, it provides high-end decorative solutions for both interior and exterior building walls.
Mara Colored Stone Parameter
| Appearance | Smooth, Flat, Delicate And Soft |
| Solid Content | 100% |
| Alkali Resistance | No Abnormalities Found In 24 Hours |
| Water Resistance | No Abnormalities Found In 48 Hours |
| Low Temperature Stability | No Abnormalities |
| Coating Temperature Resistance | No Abnormalities Were Found In The Three Cycles. |
| Paint Film Drying (surface Drying) | ≤4H |
| Recoating Time/coat Layers | ≥24H |
| Drying Time (hardening) | 72H |
Mara Colored Stone Features
1. Non-toxic and safe with multiple certifications: It adopts a non-toxic, zero-VOC dry powder formula, which does not release formaldehyde or other harmful gases. The harmful substances are
far below the national standard. It has passed multiple certifications such as the Ten-Ring Certificate and Green Building Materials Certificate. There is no odor during construction, making it suitable for highly sensitive environments such as children's rooms and hospitals.
2. Sustainable raw materials: Some components are derived from natural colored sand, inorganic minerals or recycled materials, reducing resource consumption, conforming to the concept of green building, and taking into account both environmental protection and resource recycling.
3. Crack and detachment resistant: The bonding strength is ≥0.7MPA, which combines high adhesion and flexibility. It can adapt to the thermal expansion and contraction of the wall and effectively reduce the risk of cracking and detachment in areas with large temperature differences.
4. Weather-resistant, fire-resistant, and durable: After adding exterior wall additives, it exhibits excellent resistance to artificial aging, shows no powdering after 3000 hours of testing, has a service life of 10-15 years, and meets Class A fire protection standards, thus enhancing safety.
5. High artistic and decorative appeal: The stone imitation boasts a realism of over 95%. Artificially sintered colored sand ensures stable color with no batch-to-batch variation. A 1-4mm application thickness can create three-dimensional textures, enhancing the dynamic feel of space under light and shadow.
6. Highly efficient and convenient construction: It can be directly applied to various substrates such as cement walls and gypsum boards, eliminating the need for putty leveling and primer steps, greatly simplifying the construction process and shortening the construction period by more than 30%.
For interior walls, furniture, decorations, commercial space soft furnishings, and festive decorations that require a shimmering gold effect while pursuing low pollution, as well as for living rooms, lobbies, and TV background walls, create a grand and natural artistic atmosphere.
Mara Colored Stone Construction Guidelines
1. Substrate preparation: The substrate must be flat (protrusion ≤1mm), dry and free of oil stains. Flat substrates such as gypsum board/cement walls can be directly applied without the need for putty leveling. For interface treatment, it is recommended to apply a substrate preparation agent (for loose substrates, apply a penetrating primer for reinforcement, and for dense substrates, apply a sealing primer).
2. Primer application: Apply by roller or spray, using 0.15-0.2 kg/m², drying time 2-4 hours.
3. Main material application: Apply by troweling, with a single coat thickness of 0.5-1mm, using a stainless steel trowel, apply in two coats, allowing the first coat to dry completely before applying the second coat, with a finishing window of 45-90 minutes (25℃).
4. Finishing and Topcoat: Finish the second coat when it is 80% dry to eliminate joints and bubbles,apply 0.15-0.2 kg/m² of clear topcoat to enhance stain resistance and gloss.